Ceramic Structural
Property

1.High mechanical strength

2.Good wear resistance

3.Good heat resistance

4.Corrosion resistance

Package
We can produce it according to customers'drawing.
Technical Specification
Items Specification
Density 6.03 g/cc
Bending strength 1000MPa
Fracture toughness 5~8 Mpa.m 1/2
Vickers hardness 13 Gpa
pyroconductivity 2 W/M K
linear expansion coefficient 10.5
dielectric coefficient 11*106 V/m
Yttria Stabilized Zirconia Cylinder
 
Property

1. High grinding efficiency: the specific gravity is 1.6 times more than ordinary zirconia beads,it has higher grinding efficiency under the same conditions.

2. Good fluidity. With good roundness and smooth surface ,the abrasion of the equipment is lower than other grinding media.

3. Impact resistance and low wear: with good toughness,it will don’t crack and peel in the high-speed and high-concentration machine.The wear loss is only 1/2 of zirconia silicate bead.

4. Low cost: comprehensive cost reduction of medium wear ,power consumption ,lab ,equipment etc,

Application

Paints, ink,pigment,dye

Magnetic materials,piezoelectric ceramics,Dielectric Ceramics

 Medicine,food, cosmetics 

Electric ceramics, refractory materials, structure ceramics

Package
25kgs/drum,then 200kgs/pallet
Technical Specification :
Item Specification
Composition wt% 94.5% ZrO2
5.25%  Y2O3
Compression strength ≥ 2250
Hardness Moh’s >9.0
Bulk Density Kg/L ≥3.60g/cm3
Specific Density g/cm3 ≥6.02g/cm3
 water absorption  ≤0.01%
Wear loss ≤0.01%
Color White
Available Size

7.5*7.5mm,10*10mm,12.7*12.7mm,15*15mm

Zirconia Ceramic Structures
Property

1.High mechanical strength

2.Good wear resistance

3.Good heat resistance

4.Corrosion resistance

Package
We can produce it according to customers'drawing.
Technical Specification
Items Specification
Density 6.03 g/cc
Bending strength 1000MPa
Fracture toughness 5~8 Mpa.m 1/2
Vickers hardness 13 Gpa
pyroconductivity 2 W/M K
linear expansion coefficient 10.5
dielectric coefficient 11*106 V/m
Yttria Stabilized Zirconia Cylinder
 
Property

1. High grinding efficiency: the specific gravity is 1.6 times more than ordinary zirconia beads,it has higher grinding efficiency under the same conditions.

2. Good fluidity. With good roundness and smooth surface ,the abrasion of the equipment is lower than other grinding media.

3. Impact resistance and low wear: with good toughness,it will don’t crack and peel in the high-speed and high-concentration machine.The wear loss is only 1/2 of zirconia silicate bead.

4. Low cost: comprehensive cost reduction of medium wear ,power consumption ,lab ,equipment etc,

Application

Paints, ink,pigment,dye

Magnetic materials,piezoelectric ceramics,Dielectric Ceramics

 Medicine,food, cosmetics 

Electric ceramics, refractory materials, structure ceramics

Package
25kgs/drum,then 200kgs/pallet
Technical Specification :
Item Specification
Composition wt% 94.5% ZrO2
5.25%  Y2O3
Compression strength ≥ 2250
Hardness Moh’s >9.0
Bulk Density Kg/L ≥3.60g/cm3
Specific Density g/cm3 ≥6.02g/cm3
 water absorption  ≤0.01%
Wear loss ≤0.01%
Color White
Available Size

7.5*7.5mm,10*10mm,12.7*12.7mm,15*15mm





Support:Xi Yu Technology 湘ICP备12012704号

Tel: 0086-731-84427228

Fax:0086-731-84483877

Add:No.766 Wuyi Road, Changsha, China

Support:Xi Yu Technology 湘ICP备12012704号